TECHNICAL DATA SHEET | Section 9.1
®
POLYEURO 5502
Two Component, Aromatic, Polyurea Protective Coating

Technical Data (Based on Draw Down Film)
Product Description
Polyeuro 5502 is a fast setting, rapid curing, 100% solids, Mix Ratio by Volume 1A : 1B
®
flexible, aromatic, two component spray polyurea that can be Pot Life @150-160ºF (65.5-71ºC), 50% R.H. 4-8 seconds
applied to suitably prepared concrete and metal surfaces. It 45-60 seconds
has extremely fast gel time making it suitable for applications Tack Free Time (thickness & substrate temperature dependent)
down to -20°F (-28.89°C). It may be applied in single or multiple Recoat Time 0-6 hours
applications without appreciable sagging and is relatively Viscosity at 150-160°F (65.5-71°C)
insensitive to moisture and temperature allowing application Side-A 100 ± 20 cps
in most temperatures. Polyeuro 5502 offers a tack free time of Side-B 50 ± 20 cps
®
less than sixty seconds and exhibits 400% ± 50% elongation Density (Side A & B Combined) 8.81 lbs/gal
upon curing with 50 Shore D hardness.
Flash Point > 200°F (93.3°C)
Features Hardness, ASTM D2240 50 ± 5 Shore D
• Coats Carbon or Mild Steel Metals Without Primer Tensile Strength, ASTM D412* 3000 ± 200 psi
20.68 ± 1.37 MPa
• Elastomeric
Elongation, ASTM D412* 400 ± 50%
• Excellent Thermal Stability
Tear Resistance, ASTM D624* 450 ± 50 pli
• Good Chemical Resistance 78.8 ± 8.8 kNm
• Installed With or Without Reinforcement in Transitional Service Temperature - Dry -40°F to 250°F
Areas -40°C to 121°C
Service Temperature - Wet 40°F to 120°F
• Low Temperature Flexibility 4.44°C to 48.89°C
• Meets USDA Criteria Water Vapor Permeance (Procedure B) ASTM E96 0.88 perm-inch
• Odorless Volatile Organic Compounds, (Side-A & B 0 lbs/gal
combined) ASTM D2369-81 0 gm/liter
• Seamless
Minimum Applied Thickness 1 mm
• Zero VOC (100% Solids)
Return to Service: Foot Traffic 1- 4 hours
Typical Uses Return to Service: Full Service > 24 hours
• Airports • Power Plants Taber Abrasion Resistance, ASTM D4060 (CS17 6 mg loss
wheel, 1000 cycles, 1 kg load) (maximum)
• Cold Storage Facilities • Refineries
• Secondary Containment Hydrostatic Pressure Test, ASTM D5385-93106, Pass
• Fertilizer Plants Para 7.0 Hold 100 psi
• Structural Steel
• Food Processing Plants • Walkways and Balconies Crack Bridging, ASTM C1305 (10 cycles @-15°F Pass
[-25.5°C],Rate 0.125 inch/hr, Ext. -0.125 inch)
• Industrial and • Warehouse Floors Volume Resistivity, ASTM D257 6.0 x10 ohm.cm
12
Manufacturing • Water and Wastewater
Facilities Treatment Plants Water Absorption, ASTM D471 (maximum 74°F < 2%
or 23°C, 24 hours
• Landfill Containment Impact Resistance @ 77°F or 25°C (ASTM G14) > 150 in. lbs
• Marine Environments Pull-Off Strength (minimum), ASTM D4541, Excellent
Inter-Coat Adhesion (within recoat time)
• Mining Operations
Concrete (Shot Blasted and Primed), substrate >500 psi (3.4MPa)
• Paper and Pulp Mills failure occurred
Steel (90 μm blast profile) >900 psi (6.2 MPa)
Packaging Lineal Shrinkage 1 - 2%
Flexibility (1/8” 3mm Mendrel Bend Test), Pass
10-gallon kit 5 gallons (18.9 liters) Side-A and ASTM D1737
5 gallons (18.9 liters) Side-B Resistance to Weathering, ASTM G-23 No cracking or blistering.
(Type QUV Weatherometer-3000 hrs exposure) Color change, gloss reduction
& chalking are noted.
Fire Test, ASTM E108 (Non Combustible Surface) Pass Class A
100-gallon kit 50 gallons (189 liters) Side-A and 50
gallons (189 liters) Side-B (*These physical properties from sample sprayed with Graco EXP2 @ 2000 psi minimum, with
Fusion Gun AR4242 @ 150-160°F (65°C to 71°C). Different machine and parameter will change
these properties. User should perform their own independent testing as properties are approximate).