Page 177 - Polycoat 1.1 Table of Contents

TECHNICAL DATA SHEET | Section 9.2
POLYEURO 5901
®
Two Component Aromatic Polyurea Protective Coating

Product Description
Polyeuro 5901 is a fast set, rapid curing, 100% solids, flexible, Technical Data (Based on Draw Down Film)
®
aromatic, two component spray polyurea that can be applied Mix Ratio by Volume 1A : 1B
to suitably prepared concrete and metal surfaces. Its extremely Pot Life @ 150ºF (65.5ºC), 50% R.H. 3-5-Seconds
fast gel time makes it suitable for applications down to -20°F.
It may be applied in single or multiple applications without Tack Free Time 60-120 Seconds
appreciable sagging and is relatively insensitive to moisture Recoat Time 0 - 6 hours
and temperature allowing application in most temperatures.
Viscosity at 150-160°F (65.5-71°C)
Side-A 150 ± 20 cps
Features Side-B 100 ± 20 cps
• 100% SolidsCoats Most Metals without Primer Density (Side A & B Combined) 8.70 lbs/gal
• Excellent Color Retention Flash Point > 200°F (93.3°C)
• Excellent Thermal Stability Hardness, ASTM D2240 90 ± 5 A
• Good Chemical Resistance
2500 ± 200 psi
• Installed With or Without Reinforcement in Transistional Tensile Strength, ASTM D412* 17.24 ± 1.37 MPa
AreasLow Permeance Rate
• Low Temperature Flexibility Elongation, ASTM D412* 400% ± 50%
400 ± 50 pli
• Meets USDA Criteria Tear Resistance, ASTM D412* 69.93 ± 8.8 kNm
• Non-Reactive
-40°F to 250°F
• No Toxic Vapors Service Temperature - Dry -40°C to 121°C
• Odorless
40°F to 120°F
• Seamless Service Temperature - Wet 4.44°C to 48.89°C
• Zero VOC
Water Vapor Permeability ASTM E96 1.43 Perms
Typical Uses (*These physical properties from sample sprayed with Graco Foam Cat 200 @ 2000 psi minimum,
with Gusmer GX7-400 mechanical purge gun @ 150-160°F. Different machine and parameter
• Cold Storage Facilities will change these properties. User should perform their own independent testing as properties
are approximate.).
• Fertilizer Plants
• Food Processing Plants Colors
• Industrial and Manufacturing Facilities Clear/Neutral. Custom colors are available upon request. Color
• Landfill Containment Packs, when used, must be added to Side-B.
• Marine Environments Due to its aromatic composition, Polyeuro 5901 will tend to
• Mining Operations yellow or darken in color and will become flat after expo-sure
to UV light. Polyeuro 5901 may be topcoated within twelve
• Paper and Pulp Mills hours of application with an aliphatic polyurethane/polyurea
• Parking Garage DecksPower Plants coating for a colorfast finish.
• Refineries Coverage
• Secondary Containment Polyeuro 5901 may be applied at any rate to achieve desired
• Structural Steel thickness. Theoretical coverage for 1 mil thickness is one gallon
• Walkways and Balconies per 1600 sqft.
• Warehouse Floors Surface Preparation
• Water and Waste Water Treatment In general, coating performance and adhesion are directly
proportional to surface preparation. Most failures in the
Packaging performance of surface coatings can be attributed to poor
surface preparation. Polyurea coatings rely on the structural
strength of the substrate to which they are applied. All sur-
10-gallon kit 5 gallons (18.9 liters) Side-A and faces must be free of dust, dirt, oil, grease, rust, corrosion
5 gallons (18.9 liters) Side-B and other contaminants. When coating substrates previously
used, it is important to consider the possibility of substrate
absorption, which may affect the adhesion of the coating
100-gallon kit 50 gallons (189 liters) Side-A and system, regardless of the surface preparation. Polycoat
50 gallons (189 liters) Side-B recognizes the potential for unique substrates from one project
to another. The following information is for general reference,
and for project-specific questions, contact Polycoat.

POLYCOAT PRODUCTS TEL 562.802.8834 | FAX 562.921.7363 Section 9.2
wpsales@polycoatusa.com | www.polycoatusa.com