Page 170 - Polycoat 1.1 Table of Contents

TECHNICAL DATA SHEET | Section 8.2
POLYCOAT-AQUASEAL 5000
™
Single Component, Bitumen
Modified Waterproofing Membrane Product
Approved by City of Los Angeles RR#25935

Product Description Features
Polycoat-Aquaseal 5000 is a single component, liquid applied,
™
bitumen modified, coal tar free, moisture cured polyurethane • Economical
waterproofing membrane. The standard Polycoat-Aquaseal • Labor Saving
™
5000 may be applied to both fully cured concrete (28 days for
poured in place and 10 days after grouting for block). Polycoat- • Meets the Criteria of ASTM C836 and E96
Aquaseal 5000GC may be applied to Green Concrete. For • Resistant to Bacteria
™
Green Concrete, GC Additive must be added to Polycoat-
Aquaseal 5000 at a ratio of ½ pint GC Additive (256 ml) to 5 • User Friendly
™
gallons (18.9 liters) of Polycoat-Aquaseal 5000. Thoroughly
™
mix with a variable speed drill and mixing paddle at slow Typical Uses
speed.
• Basements • Planters
It is available in four application versions. For 28-day cured
concrete Horizontal (H) and Vertical (V) grade versions should • Between Slabs • Shower Pans
be used. For Green Concrete (GC) Horizontal (GCH) and Vertical • Bridges • Tunnels
™
(GCV) grade versions are used. Polycoat-Aquaseal 5000 has
VOC levels equal to or less than 100 grams per liter. Make • Foundation Walls
sure to use the correct grade of product which complies with
VOC regulations/requirements applicable as per federal, state,
statutory, counties, cities and local bodies at the place of Packaging
installation.
5-Gallon 5 gallon (18.9 liter) pail
Color
Black
55-Gallon 55 gallon drum, net fill 50 gallons (189
Coverage liters)
The approximate coverage is 2 gallons/100 per sqft (0.41l/
sqft) or 100 sqft/gallon which results in a dry film thickness of
28 mils (355 microns). Coverage rate will depend on surface
roughness and porosity.
Surface Preparation
Refer to General Guidelines for complete information. recommended primer.
Joints, Cracks and Flashing: Mixing
™
Apply a stripe coat of Polycoat-Aquaseal 5000 over all cracks Before application, Polycoat-Aquaseal 5000 should be
™
up to 1/16” (1.58 mm) width. All cracks over 1/16” (1.58 mm) thoroughly mixed using a mechanical mixer at slow speed
width must be caulked with a polyurethane sealant. to ensure a homogeneous material. Take care not to allow
entrapment of air into the material. Do not mix in an up and
All metal flashings must be primed with manufacturer’s
down motion.
™
Technical Data (Based on Draw Down Film) Polycoat-Aquaseal 5000 Properties
5000H 5000V 5000GCH 5000GCV
HORIZONTAL VERTICAL HORIZONTAL VERTICAL
Hardness, ASTM D2240 50 ± 5 Shore A 45 ± 5 Shore A 50 ± 5 Shore A 45 ± 5 Shore A
Tear Resistance, Die C, ASTM D624 70 ± 20 pli 100 ± 20 pli 70 ± 20 pli 100 ± 20 pli
9.3 ± 2.6 kN/m 13.3 ± 2 kN/m 9.3 ± 2.6 kN/m 13.3 ± 2 kN/m
Tensile Strength, ASTM D412 450 ± 50 psi 500 ± 50 psi 450 ± 50 psi 500 ± 50 psi
3.1 ± 0.3 MPa 3.4 ± 0.3 MPa 3.1 ± 0.3 MPa 3.4 ± 0.3 MPa
Ultimate Elongation, ASTM D412 500 ± 50% 500 ± 50% 450 ± 50% 450 ± 50%
Specific Gravity 1.28 ± 0.1 1.20 ± 0.3 1.28 ± 0.1 1.20 ± 0.1
Total Solids by Weight, ASTM D2369 95 ± 3% 91 ± 3% 95 ± 3% 91 ± 3%
Total Solids by Volume, ASTM D2697 94 ± 3% 89 ± 3% 94 ± 3% 89 ± 3%
Viscosity at 80°F (27°C) 5000 ± 2000 cps 40,000 ± 20,000 cps 5000 ± 2000 cps 40,000 ± 2000 cps
Volatile Organic Compounds, ASTM D2369-81 0.83 lb/gal, 0.83 lb/gal, 0.83 lb/gal, 0.83 lb/gal,
100 gm/liter 100 gm/liter 100 gm/liter 100 gm/liter
Service Temperature -25°F to 200°F -25°F to 200°F -25°F to 200°F -25°F to 200°F
-31.7°C to 65°C -31.7°C to 65°C -31.7°C to 65°C -31.7°C to 65°C

POLYCOAT PRODUCTS TEL 562.802.8834 | FAX 562.921.7363 Section 8.2