Page 23 - tmp

TECHNICAL DATA SHEET
®
THEMECOAT 752
Two Component Aromatic Hybrid
Polyurethane Protective Coating

PRODUCT DESCRIPTION
Themecoat 752 is a fast setting, rapid curing, aromatic, two TECHNICAL DATA (Based on Draw Down Films)
®
component, hybrid polyurea/polyurethane spray designed Mix Ratio 1A : 1B
to be applied over EPS, wood and many other surfaces. Its
excellent balance of stiffness and impact resistance provides Pot Life 2-4 seconds
excellent plastic “shell-like” protection for delicate foams Tack Free Time 60-120 seconds
and EPS. Themecoat 752’s chemical design allows fast “user-
®
friendly” application with excellent flow and appearance. Recoat Time 0-12 hours
Themecoat 752 offers a tensile strength of 3700 psi (26 MPa) Viscosity at 150-160ºF
®
upon curing with 75 Shore D hardness. (66.6-71ºC), Brookfield:
90 ± 20 cps
FEATURES Side-A 160 ± 20 cps
Side-B
• 100% Solids
9.03 lbs/gal
• Excellent Chemical Protection Density (Side A & B (1230 kgs/m )
Combined)
3
• Excellent Cold Temperature Impact
>200ºF
• Excellent Thermal Stability Flash Point (>93.3ºC)
• Fast Cure
• High Productivity Hardness, ASTM D-2240* 75 ± 5%
• Low Shrinkage Tensile, ASTM 412-C* 3700 ± 200 psi
• Meets USDA Criteria (26 ± 1.4 MPa)
• Plastic “Shell-Like” Protection Elongation, ASTM 412-C* 40% ± 20%
• Zero VOC
Tear, ASTM 624-C* 450 ± 50 pli
TYPICAL USES (79 ± 8.8 kN/m)
• Architectural Shapes Service Temperature - Dry -20ºF to 250ºF
• Decorations / Props (-29-121ºC)
• Dock Flotations Service Temperature - Wet 40ºF to 120ºF
• Food Processing Plants (4.4-49ºC)
• Speaker Boxes
• Steel Coating (*These physical properties from sample sprayed with Graco Foam Cat
• Wood Cabinets 200 @ 2000 psi (32 MPa) minimum, with Gusmer GX7-400 mechanical
purge gun @ 150-160°F (66-72ºC). Different machine and parameter will
• Wood Pallets / Crates change these properties. User should perform their own independent
testing as properties are approximate).
PACKAGING
10-gallon kit: 5 gallon (18.9 liters) pail of Side-A and 5-gallon
(18.9 liters) pail of Side-B.
be free of dust, dirt, oil, grease, rust, corrosion and other
100-gallon kit: 50 gallon (189 liters) drum of Side-A and contaminants. When coating substrates previously used, it is
50-gallon (189 liters) drum of Side-B. important to consider the possibility of substrate absorption,
which may affect the adhesion of the coating system, regard-
COLORS less of the surface preparation. Polycoat recognizes the
Clear/Neutral/Tan. Custom colors are available upon request. potential for unique substrates from one project to another.
Color Packs, when used, must be added to Side-B. The following information is for general reference, and for
Due to its aromatic composition, Themecoat 752 will tend to project-specific questions, contact Polycoat
®
yellow or darken in color and will become flat after exposure NEW AND OLD CONCRETE:
to UV light. Themecoat 752 may be topcoated within twelve Refer to SSPC-SP13/NACE 6, or ICRI 03732: CSP 3-5. New
®
hours of application with an aliphatic polyurethane/polyurea concrete must be cured for 28 days prior to product applica-
coating for a colorfast finish. tion. Surface must be clean, dry, sound and offer sufficient
COVERAGE profile for product adhesion. Remove all dust, dirt, oil, form
Themecoat 752 may be applied at any rate to achieve desired release agents, curing compounds, salts, efflorescence,
®
thickness. Theoretical coverage for 1 mil thickness is one laitance and other foreign matter by shotblasting and/or
gallon per 1600 sqft (3.78 liters per 149 sqm). suitable chemical means, in accordance with local chemical
regulations. Rinse thoroughly, to achieve a pH between 8.0 and
SURFACE PREPARATION 11.0. Allow to dry completely. If old concrete has a surface that
In general, coating performance and adhesion are directly has deteriorated to an unacceptably rough surface, Polycoat
®
proportional to surface preparation. Most failures in the perfor- Products PC-260 or a mixture of Polyprime 21 and sand
mance of surface coatings can be attributed to poor surface should be used as a repair agent for cracks, spalls, bug holes
preparation. Polyurea coatings rely on the structural strength and voids. Upon full cure of the repair agent, prime the entire
of the substrate to which they are applied. All surfaces must surface intended for coating.