TECHNICAL DATA SHEET
THEMECOAT 750-FLEX
®
Two Component Aromatic Hybrid
Polyurethane Protective Coating

PRODUCT DESCRIPTION TECHNICAL DATA (Based on Draw Down Films)
Themecoat 750 Flex is a fast setting, rapid curing, aromatic,
®
two component, hybrid polyurea/polyurethane spray designed Mix Ratio 1A : 1B
to be applied over EPS, wood and many other surfaces.
Pot Life 10-15 seconds
Its excellent balance of stiffness and impact resistance provides
excellent plastic “shell-like” protection for delicate foams and Tack Free Time 60-120 seconds
EPS. Themecoat 750 Flex’s chemical design allows fast “user- Recoat Time 0-12 hours
®
friendly” application with excellent flow and appearance.
Viscosity at 150-160ºF
FEATURES (66.6-71ºC), Brookfield:
• 100% Solids Side-A 90 ± 20 cps
• Excellent Chemical Protection Side-B 160 ± 20 cps
• Excellent Cold Temperature Impact Density (Side A & B Combined) 9.03 lbs/gal
3
• Excellent Thermal Stability (1230 kgs/m )
• Fast Cure Flash Point >200ºF
• High Productivity (>93.3ºC)
• Low Shrinkage Hardness, ASTM D-2240* 65 ± 5%
• Meets USDA Criteria Tensile, ASTM 412-C* 3500 ± 300 psi
• Offers More Flexibility (24 ± 2.1 MPa)
• Plastic “Shell-Like” Protection Elongation, ASTM 412-C* 70% ± 20%
• Zero VOC
Tear, ASTM 624-C* 450 ± 50 pli
TYPICAL USES (79 ± 8.8 kN/m)
• Architectural Shapes Service Temperature - Dry -20ºF to 250ºF
• Decorations / Props (-29-121ºC)
• Dock Flotations 40ºF to 120ºF
• Food Processing Plants Service Temperature - Wet (4.4-49ºC)
• Speaker Boxes
• Steel Coating (*These physical properties from sample sprayed with Graco Foam Cat
• Wood Cabinets 200 @ 2000 psi (32 MPa) minimum, with Gusmer GX7-400 mechanical
• Wood Pallets / Crates purge gun @ 150-160°F (66-72ºC). Different machine and parameter will
change these properties. User should perform their own independent
testing as properties are approximate).
PACKAGING
10-gallon kit: 5 gallon (18.9 liters) pail of Side-A and 5-gallon
(18.9 liters) pail of Side-B.
be free of dust, dirt, oil, grease, rust, corrosion and other
100-gallon kit: 50 gallon (189 liters) drum of Side-A and contaminants. When coating substrates previously used, it is
50-gallon (189 liters) drum of Side-B. important to consider the possibility of substrate absorption,
which may affect the adhesion of the coating system, regard-
COLORS less of the surface preparation. Polycoat recognizes the
Clear/Neutral/Tan. Custom colors are available upon request. potential for unique substrates from one project to another.
Color Packs, when used, must be added to Side-B. The following information is for general reference, and for
®
Due to its aromatic composition, Themecoat 750 Flex will tend project-specific questions, contact Polycoat
to yellow or darken in color and will become flat after exposure NEW AND OLD CONCRETE:
®
to UV light. Themecoat 750 Flex may be topcoated within Refer to SSPC-SP13/NACE 6, or ICRI 03732: CSP 3-5. New
twelve hours of application with an aliphatic polyurethane/ concrete must be cured for 28 days prior to product applica-
polyurea coating for a colorfast finish. tion. Surface must be clean, dry, sound and offer sufficient
COVERAGE profile for product adhesion. Remove all dust, dirt, oil, form
Themecoat 750-Flex may be applied at any rate to achieve release agents, curing compounds, salts, efflorescence,
®
desired thickness. Theoretical coverage for 1 mil thickness is laitance and other foreign matter by shotblasting and/or
one gallon per 1600 sqft (3.78 liters per 149 sqm). suitable chemical means, in accordance with local chemical
regulations. Rinse thoroughly, to achieve a pH between 8.0 and
SURFACE PREPARATION 11.0. Allow to dry completely. If old concrete has a surface that
In general, coating performance and adhesion are directly has deteriorated to an unacceptably rough surface, Polycoat
®
proportional to surface preparation. Most failures in the perfor- Products PC-260 or a mixture of Polyprime 21 and sand should
mance of surface coatings can be attributed to poor surface be used as a repair agent for cracks, spalls, bug holes and
preparation. Polyurea coatings rely on the structural strength voids. Upon full cure of the repair agent, prime the entire
of the substrate to which they are applied. All surfaces must surface intended for coating.