Page 25 - tmp

TECHNICAL DATA SHEET
THEMECOAT 752-FR
®
Fire Retardant Two Component Aromatic Hybrid
Polyurethane Protective Coating

PRODUCT DESCRIPTION TECHNICAL DATA (Based on Draw Down Films)
Themecoat 752-FR is a fire-rated, fast set, rapid curing,
®
aromatic, two component hybrid polyurea/polyurethane Mix Ratio 1A : 1B
spray designed to be applied over EPS, wood, and many Pot Life 4-6 seconds
other surfaces. Its excellent balance of stiffness and impact
resistance provides excellent plastic “shell-like” protection Tack Free Time 60-120 seconds
for delicate foams and EPS. Themecoat 752-FR’s chemical Recoat Time 0-12 hours
®
design allows fast “user-friendly” application with excellent
flow and appearance. Viscosity at 150-160ºF
(66.6-71ºC), Brookfield:
FEATURES Side-A 150 ± 20 cps
• 100% Solids Side-B 250 ± 50 cps
• Excellent Chemical Protection Density (Side A & B 10.89 lbs/gal
3
• Excellent Cold Temperature Impact Combined) (1300 kgs/m )
• Excellent Thermal Stability Flash Point >200ºF
• Fast Cure (>93.3ºC)
• High Productivity Hardness, ASTM D-2240* 75 ± 5%
• Low Shrinkage
• Meets USDA Criteria Tensile, ASTM 412-C* 2500 ± 200 psi
• Plastic “Shell-Like” Protection (17 ± 1.4 MPa)
• Zero VOC Elongation, ASTM 412-C* 10% ± 2%
TYPICAL USES Tear, ASTM 624-C* 400 ± 30 pli
• Architectural Shapes (70 ± 5.7 kN/m)
• Decorations / Props Service Temperature - Dry -40ºF to 300ºF
• Dock Flotations (-40-149ºC)
• Food Processing Plants Service Temperature - Wet 40ºF to 120ºF
• Speaker Boxes (4.4-49ºC)
• Steel Coating (*These physical properties from sample sprayed with Graco Foam Cat
• Wood Cabinets 200 @ 2000 psi (32 MPa) minimum, with Gusmer GX7-400 mechanical
• Wood Pallets / Crates purge gun @ 150-160°F (66-72ºC). Different machine and parameter will
change these properties. User should perform their own independent
PACKAGING testing as properties are approximate).
10-gallon kit: 5 gallon (18.9 liters) pail of Side-A and 5-gallon
(18.9 liters) pail of Side-B.
100-gallon kit: 50 gallon (189 liters) drum of Side-A and be free of dust, dirt, oil, grease, rust, corrosion and other
50-gallon (189 liters) drum of Side-B. contaminants. When coating substrates previously used, it is
important to consider the possibility of substrate absorption,
COLORS which may affect the adhesion of the coating system, regard-
Clear/Neutral/Tan. Custom colors are available upon request. less of the surface preparation. Polycoat recognizes the
Color Packs, when used, must be added to Side-B. potential for unique substrates from one project to another.
Due to its aromatic composition, Themecoat 752-FR will tend The following information is for general reference, and for
®
to yellow or darken in color and will become flat after exposure project-specific questions, contact Polycoat
to UV light. Themecoat 752-FR may be topcoated within NEW AND OLD CONCRETE:
®
twelve hours of application with an aliphatic polyurethane/ Refer to SSPC-SP13/NACE 6, or ICRI 03732: CSP 3-5. New
polyurea coating for a colorfast finish. concrete must be cured for 28 days prior to product applica-
COVERAGE tion. Surface must be clean, dry, sound and offer sufficient
Themecoat 752-FR may be applied at any rate to achieve profile for product adhesion. Remove all dust, dirt, oil, form
®
desired thickness. Theoretical coverage for 1 mil thickness is release agents, curing compounds, salts, efflorescence,
one gallon per 1600 sqft (3.78 liters per 149 sqm). laitance and other foreign matter by shotblasting and/or
suitable chemical means, in accordance with local chemical
SURFACE PREPARATION regulations. Rinse thoroughly, to achieve a pH between 8.0 and
In general, coating performance and adhesion are directly 11.0. Allow to dry completely. If old concrete has a surface that
proportional to surface preparation. Most failures in the perfor- has deteriorated to an unacceptably rough surface, Polycoat
mance of surface coatings can be attributed to poor surface Products PC-260 or a mixture of Polyprime 21 and sand should
®
preparation. Polyurea coatings rely on the structural strength be used as a repair agent for cracks, spalls, bug holes and
of the substrate to which they are applied. All surfaces must voids. Upon full cure of the repair agent, prime the entire