Page 113 - Polycoat 1.1 Table of Contents

Note: a) Of the 18 reagents used in the chemical resistance 3. One-Hour Fire-Resistive Construction: Based on the
test, only sulfuric acid concentrate caused a deterioration of performance of the test assembly, Polydeck 400 Walking Deck

the decking system. System installed on p" thick C-D plywood as a substitute for the
b) Wearing surface revealed no cracking, crazing, double wood floor described in Construction No. 13, Item 13-

delamination, or any other deleterious effects. 1.1, Table No. 7-C of the 1994 U.B.C. Standard No. 7-1. The

c) The test specimens which were coded “No. 3 - assembly was tested with 2 x 10 floor joists spaced at 16 inches

Considerably Affected” could not be restored to their original on center.

surface condition by normal cleaning methods.
The average room temperature rise on the unexposed face was
260°F and the maximum single thermometer reading was
11. Low Temperature Flexibility: AC 39 Sec. K. 5°F. No 310°F after 65 minutes. The acceptance limit is 250°F average
cracking or crazing upon visual examination under 5x temperature rise with no single reading over 350°F above

magnification in the bent condition. ambient after 60 minutes. The area under the test time v.
temperature curve equals the standard time-temperature E-119
12. Fire Resistance Test Class “A”: U.B.C. Standard 32-7, curve at 60.56 minutes.

ASTM E-108, U.L.790, N.F.P.A. No. 256, on p" (1.9 cm)

plywood.
A) Intermittent Flame Exposure Test (2 decks): Both of the

decks met the requirements for Class “A” Intermittent Flame

Exposure Test. There was no evidence of displacement,

sliding, spalling, or flames underneath these decks during or
after the test.
B) Spread of Flame Test (2 decks): Base (in.) Length (in.)
Deck 1 21 54
Deck 2 18 43
Max. Flame Spread Allowed 40 72

C) Burning Brand Test (4 decks): All passed. The heat areas
were confined to the immediate area of brand placement.
There was no displacement of the Polydeck 400 System
observed during or after the test. Material flaming underneath
the decks did occur, but all self extinguished within the
allotted testing time.

Polydeck 400 will satisfactorily withstand the three methods
of tests for a Class A rating on concrete substrates and Class
A Rating on p" plywood in UBC STD #32-7, ASTM E108, UL
790 and NFPA No. 256, when constructed, installed and
tested as described herein.

______________________________________________________________________________________________________________________________________
Limited Warranty:
Please read all information in the general guidelines, product data sheets, guide specifications and material safety data sheets (MSDS) before applying material. Published technical data and instructions are subject to
change without notice. Contact your local Polycoat Products representative or visit our website for current technical data and instructions.

Polycoat Products warrants its products to be free of manufacturing defects and that they will meet Polycoat Products current published physical properties. Polycoat Products warrants that its products, when properly installed by a state
licensed waterproofing contractor according to Polycoat Products guide specifications and product data sheets over a sound, properly prepared substrate, will not allow water migration for a period of one (1) year. Seller’s and
manufacturer’s sole responsibility shall be to replace that portion of the product of this manufacturer which proves to be defective. There are no other warranties by Polycoat Products of any nature whatsoever expressed or implied,
including any warranty of merchantability or fitness for a particular purpose in connection with this product. Polycoat Products shall not be liable for damages of any sort, including remote or consequential damages resulting from any
claimed breach of any warranty whether expressed or implied. Polycoat Products shall not be responsible for use of this product in a manner to infringe on any patent held by others. In addition, no warranty or guarantee is being issued
with respect to appearance, color, fading, chalking, staining, shrinkage, peeling, normal wear and tear or improper application by the applicator. Damage caused by abuse, neglect and lack of proper maintenance, acts of nature and/or
physical movement of the substrate or structural defects are also excluded from the limited warranty. Polycoat Products reserves the right to conduct performance tests on any material claimed to be defective prior to any repairs by owner,
general contractor, or applicator.

Disclaimer:
All guidelines, recommendations, statements, and technical data contained herein are based on information and tests we believe to be reliable and correct, but accuracy and completeness of said tests are not guaranteed and are not to be
construed as a warranty, either expressed or implied. It is the users responsibility to satisfy himself, by his own information and test, to determine suitability of the product for his own intended use, application and job situation and user
assumes all risk and liability resulting from his use of the product. We do not suggest or guarantee that any hazard listed herein are the only ones which may exist. Neither seller nor manufacturer shall be liable to the buyer or any third
person for any injury, loss or damage directly or indirectly resulting from use of, or inability to use, the product. Recommendations or statements, whether in writing or oral, other than those contained herein shall not be binding upon the
manufacturer, unless in writing and signed by a corporate officer of the manufacturer. Technical and application information is provided for the purpose of establishing a general profile of the material and proper application procedures.
Test performance results were obtained in a controlled environment and Polycoat Products makes no claim that these tests or any other tests, accurately represent all environments.

®
Testing & Approvals - Polydeck 400 Page 2 of 2

14722 Spring Ave  Santa Fe Springs, CA 90670-5108 USA  Tel: 562-802-8834  Fax: 562-921-7363  www.polycoatusa.com  Copyright ® November 2012 Polycoat Products