TECHNICAL DATA SHEET I SECTION 3.10
POLYEURO 5901
®
Two Component Aromatic Polyurea Protective Coating

Product Description Technical Data
Polyeuro 5901 is a fast set, rapid curing, 100% solids, flexible,
®
aromatic, two component spray polyurea that can be applied Mix Ratio by Volume 1A : 1B
to suitably prepared concrete and metal surfaces. Its extremely Pot Life @ 150ºF (65.5ºC), 50% R.H. 3-5-Seconds
fast gel time makes it suitable for applications down to -20°F
(-28.9°F). It may be applied in single or multiple applications Tack Free Time 60-120 Seconds
without appreciable sagging and is relatively insensitive Recoat Time 0 - 6 hours
to moisture and temperature allowing application in most
temperatures. Viscosity at 150-160°F (65.5-71°C) 150 ± 20 cps
Side-A
Side-B 100 ± 20 cps
Features
Density (Side-A & Side-B Combined) 8.70 lbs/gal
• 100% Solids
• Coats Most Metals without Primer Flash Point > 200°F (93.3°C)
• Excellent Color Retention Hardness, ASTM D2240 90 ± 5 A
• Excellent Thermal Stability Tensile Strength, ASTM D412* 2500 ± 200 psi
• Good Chemical Resistance 17.24 ± 1.37 MPa
• Installed With or Without Reinforcement in Transistional Elongation, ASTM D412* 400% ± 50%
AreasLow Permeance Rate Tear Strength, ASTM D624* 400 ± 50 pli
• Low Temperature Flexibility 69.93 ± 8.8 kNm
• Meets USDA Criteria Service Temperature - Dry -40°F to 250°F
• Non-Reactive -40°C to 121°C
• No Toxic Vapors Service Temperature - Wet 40°F to 120°F
• Odorless 4.44°C to 48.89°C
• Seamless Water Vapor Permeability ASTM E96 1.43 Perms
• Zero VOC *These physical properties from sample sprayed with Graco Foam Cat 200 @ 2000 psi minimum,
with Gusmer GX7-400 mechanical purge gun @ 150-160°F. Different machine and parameter
Typical Uses will change these properties. User should perform their own independent testing as properties
are approximate.
• Cold-Storage Facilities Colors
• Fertilizer Plants Clear/Neutral. Custom colors are available upon request. Color
• Food-Processing Plants Packs, when used, must be added to Side-B.
• Industrial and Manufacturing Facilities Due to its aromatic composition, Polyeuro 5901 will tend to
• Landfill Containment yellow or darken in color and will become flat after expo-sure
• Marine Environments to UV light. Polyeuro 5901 may be topcoated within twelve
• Mining Operations hours of application with an aliphatic polyurethane/polyurea
• Paper and Pulp Mills coating for a colorfast finish.
• Parking-Garage Decks Coverage
• Power Plants Polyeuro 5901 may be applied at any rate to achieve desired
• Refineries thickness. Theoretical coverage for 1 mil (0.254 microns)
• Secondary Containment thickness is one gallon per 1600 sqft (3.78 liters per 149 sqm).
• Structural Steel Estimating Formula: (1600 sqft per gal /Dry Mil Thickness) x
• Walkways and Balconies Solids Content = Application Rate per gallon.
• Warehouse Floors Surface Preparation
• Water and Waste Water Treatment In general, coating performance and adhesion are directly
proportional to surface preparation. Most failures in the
performance of surface coatings can be attributed to poor
Packaging surface preparation. Polyurea coatings rely on the structural
strength of the substrate to which they are applied. All sur-
10-gallon kit 5 gallons (18.9 liters) Side-A and 5 faces must be free of dust, dirt, oil, grease, rust, corrosion
gallons (18.9 liters) Side-B and other contaminants. When coating substrates previously
used, it is important to consider the possibility of substrate
100-gallon kit 50 gallons (189 liters) Side-A and 50 absorption, which may affect the adhesion of the coating
gallons (189 liters) Side-B system, regardless of the surface preparation. Polycoat
recognizes the potential for unique substrates from one project
to another. The following information is for general reference,
and for project-specific questions, contact Polycoat.