Page 41 - tmp

TECHNICAL DATA SHEET I SECTION 3.4
POLYEURO 5502
®
Two Component, Aromatic,
Polyurea Protective Coating

Product Description Technical Data
Polyeuro 5502 is a fast setting, rapid curing, 100% solids,
®
flexible, aromatic, two component, spray polyurea that can be Mix Ratio by Volume 1A : 1B
applied to suitably prepared concrete and metal surfaces. It Pot Life @150-160ºF (65.5-71ºC), 50% R.H. 4-8 seconds
has extremely fast gel time making it suitable for applications
down to -20°F (-28.89°C). It may be applied in single or multiple Tack Free Time (thickness & substrate temperature dependent) 45-60 seconds
applications without appreciable sagging and is relatively Recoat Time 0-6 hours
insensitive to moisture and temperature allowing application
in most temperatures. Polyeuro 5502 offers a tack free time of Viscosity at 150-160°F (65.5-71°C)
®
Side-A
less than sixty seconds and exhibits 400% ± 50% elongation Side-B 100 ± 20 cps
50 ± 20 cps
upon curing with 50 Shore D hardness.
Density (Side-A & Side-B Combined) 8.81 lbs/gal
Features Flash Point > 200°F (93.3°C)
• Coats Carbon or Mild Steel Metals Without Primer Hardness, ASTM D2240 50 ± 5 Shore D
• Elastomeric Tensile Strength, ASTM D412* 3000 ± 200 psi
• Excellent Thermal Stability 20.68 ± 1.37 MPa
• Good Chemical Resistance Elongation, ASTM D412* 400 ± 50%
• Installed With or Without Reinforcement in Transitional Tear Strength, ASTM D624* 450 ± 50 pli
Areas 78.8 ± 8.8 kNm
• Low Temperature Flexibility Service Temperature - Dry -40°F to 250°F
• Meets USDA Criteria -40°C to 121°C
• Odorless Service Temperature - Wet 40°F to 120°F
• Seamless 4.44°C to 48.89°C
• Zero VOC (100% Solids) Water Vapor Permeance (Procedure B) ASTM E96 0.88 perm-inch
Volatile Organic Compounds, (Side-A & B 0 lbs/gal
Typical Uses combined) ASTM D2369-81 0 gm/liter

• Cold-Storage Facilities Minimum Applied Thickness 1 mm
• Fertilizer Plants Return to Service: Foot Traffic 1- 4 hours
• Food-Processing Plants Return to Service: Full Service > 24 hours
• Industrial and Manufacturing Facilities Taber Abrasion Resistance, ASTM D4060 (CS17 6 mg loss
• Landfill Containment wheel, 1000 cycles, 1 kg load) (maximum)
• Manholes Hydrostatic Pressure Test, ASTM D5385-93106, Pass
• Marine Environments Para 7.0 Hold 100 psi
• Mining Operations Crack Bridging, ASTM C1305 (10 cycles @-15°F Pass
[-25.5°C],Rate 0.125 inch/hr, Ext. -0.125 inch)
• Paper and Pulp Mills
12
• Parking Garage Decks Volume Resistivity, ASTM D257 6.0 x10 ohm.cm
• Pen Stocks Water Absorption, ASTM D471 (maximum 74°F < 2%
or 23°C, 24 hours
• Power Plants
• Refineries Impact Resistance @ 77°F or 25°C (ASTM G14) > 150 in. lbs
• Secondary Containment Pull-Off Strength (minimum), ASTM D4541, Excellent
• Structural Steel Inter-Coat Adhesion (within recoat time)
• Walkways and Balconies Concrete (Shot Blasted and Primed), substrate >500 psi (3.4MPa)
failure occurred
• Warehouse Floors
Steel (90 μm blast profile) >900 psi (6.2 MPa)
Packaging Lineal Shrinkage 1 - 2%
Flexibility (1/8” 3mm Mendrel Bend Test), Pass
10-gallon kit 5 gallons (18.9 liters) Side-A and 5 ASTM D1737
gallons (18.9 liters) Side-B Resistance to Weathering, ASTM G-23 No cracking or blistering.
(Type QUV Weatherometer-3000 hrs exposure) Color change, gloss reduction
& chalking are noted.
100-gallon kit 50 gallons (189 liters) Side-A and 50
gallons (189 liters) Side-B Fire Test, ASTM E108 (Non Combustible Surface) Pass Class A
*These physical properties from sample sprayed with Graco EXP2 @ 2000 psi minimum, with
Fusion Gun AR4242 @ 150-160°F (65°C to 71°C). Different machine and parameter will change
these properties. User should perform their own independent testing as properties are approximate.

POLYCOAT PRODUCTS TEL 562.802.8834 | FAX 562.921.7363 Section 3.4