TECHNICAL DATA SHEET I SECTION 2.6
POLYPRIME EBF-LV
®
Two Component, High Solids,
Epoxy-Polyamine Filler Surfacer Primer
Product Description
Polyprime EBF-LV is a two component, high solids, liquid Technical Data (Based on Draw Down Film)
®
applied, epoxy-polyamine filler surfacer with unique
characteristics of sealing pores in concrete. Coverage Rate 1 gal/200 sqft
0.20 l/sqm
Features
Dry Film Thickness per 7 ± 1 mils
• Excellent Adhesion Coat 48 ± 25 microns
• High Solids
• Low Odor Mixing Ratio 1A:1B
• Solvent Free
Pot Life at 75ºF (24ºC), 30-45 min
Typical Uses 50% RH
• Concrete Hardness, ASTM D2240 70 ± 5 Shore D
• Polyurethane Elastomeric Surfaces
• Steel
Specific Gravity,
Side-A 1.34 ± 0.1
Side-B 1.96 ± 0.1
Packaging
2-Gallon Kit One 1 gallon (3.78 liters) can Total Solids by Weight, 94.5 ± 2%
of Side-A and One 1 gallon ASTM D2369
(3.78 liters) can of Side-B
Total Solids by Volume, 91.4 ± 2%
10-Gallon Kit One 5 gallon (18.9 liters) pail ASTM D2697
of Side-A and One 5 gallon
(18.9 liters) pail of Side-B Viscosity at 75°F (24°C) 3000 ± 200 cps
Color
Side-A: Black, Side-B: White
Application
Coverage Polyprime EBF-LV should be used on rough or porous
®
The approximate coverage is 1 gallon/200sqft (0.20 l/sqm) concrete, or when outgassing is a concern. Polyprime EBF-
®
or 200 sqft/gallon. Coverage rate will depend on surface LV can be applied using a flat squeegee, phenolic resin core
roughness and porosity. roller, trowel or airless spray.
Surface Preparation Finishing
Remove all contaminant, oil and grease from substrate. Refer Allow Polyprime EBF-LV to become tack free before applying
®
to General Guidelines for complete information. the coating. Approximate tack free time is 3-5 hours at 75°F
(24°C) and 50% relative humidity. If the primer has been
Mixing allowed to remain tack free for more than 12 hours, it is
The volume mixing ratio is 1 part Side-A to 1 part Side-B necessary to solvent wipe surface with VOC-compliant solvent
(1A:1A). Do not mix in an up and down motion. and re-prime the surface.
Polyprime EBF-LV Side-A and Side-B should be thoroughly Recommended surface temperature should be greater than
®
mixed individually prior to combining to ensure a 50°F (10°C) and at least 5°F (3°C) above the dew point.
homogeneous material. Polyprime EBF-LV must always be
®
mixed with one part Side-A and one part Side-B (1A:1B). The Polyprime EBF-LV is very sensitive to heat. Higher
®
combined components should be thoroughly mixed using a temperatures will significantly accelerate the cure time and
mechanical mixer at slow speed. pot life. Use caution in batch sizes and thickness of application.