TECHNICAL DATA SHEET
THEMECOAT POLYPRIME 130
®
Two Component Polyurethane Primer
PRODUCT DESCRIPTION
Themecoat Polyprime 130 is a two component, liquid applied, TECHNICAL DATA (Based on Draw Down Films)
®
urea polyurethane primer.
Coverage Rate 1 gal/300 sqft (0.14 l/m )
2
FEATURES Mixing Ratio by Volume 1A:3B
• Low Order Pot Life at 75ºF (24ºC), 50% 40-60 minutes
RH
• Quick Drying
Dry Film Thickness per Coat 3 ±1 mils
(76 ± 25 microns)
TYPICAL USES Hardness, ASTM D-2240 70 ± 5 D
• Metal
• Glass Reinforced Plastics Specfic Gravity 1.06
Side-A
• Polyurethane Elastomeric Surfaces Side-B 1.47
Total Solids by Weight, 75 ± 3%
PACKAGING ASTM D-2369
1-gallon kit: 1 quart can of Side-A, net 0.25 gallon (0.95 liter) Total Solids by Volume, 62 ± 3%
and three - 1 quart cans of Side-B Off-White Liquid, net 0.25 ASTM D-2697
gallon (0.95 liter) Viscosity, cps at 75ºF (24ºC)
500 ± 200
4-gallon kit: 1 gallon can of Side-A Clear Liquid, net 1 gallon Side-A 2500 ± 500
Side-B
(3.78 liter) and One - 5 gallon pail of Side-B Off-White Liquid,
net 3 gallon (11.34 liter). VOC, ASTM D-2369-81 0.21 lb/gal
(25 gm/liter)
COLORS
Side-A: Clear, Side-B: Off-White Themecoat Polyprime 130 is very sensitive to heat and
®
moisture. Higher temperatures and/or high humidity will
COVERAGE significantly accelerate the cure time and pot life. Use caution
in batch sizes and thickness of application. Low temperature
Approximate coverage is one gallon per 300 per sqft (0.14 and/or low humidity extend the cure time.
2
l/m ).
SURFACE PREPARATION STORAGE
®
Themecoat Polyprime 130 has a shelf life of one (1) year from
Remove all contaminant, oil and grease from substrate. date of manufacture in original, factory sealed containers.
MIXING Side-A and Side-B must be stored above 60°F (15°C).
Mix no more material than can be used within 20 minutes. Avoid freezing temperatures.
Themecoat Polyprime 130 may not be diluted under any
®
circumstance. The volume mixing ratio: 1 part Side-A to 3 Store containers on wooden pallets to avoid direct contact
parts Side-B. Mix no more material than can be used within with the ground.
20 minutes. Themecoat Polyprime 130 Side-B should be Do not store outside.
®
thoroughly mixed prior to combining to ensure a homogeneous
material. The combined components should be thoroughly
mixed using a mechanical mixer at slow speed or for at least LIMITATIONS
5 minutes if mixed by hand. Not UV stable.
APPLICATION Cannot withstand direct wear or abrasion.
Mix no more material than can be used within 20 minutes. Containers that have been opened must be used as soon as
Themecoat Polyprime 130 should be applied at the rate of 1 possible.
®
gallon (mixture of Side-A & Side-B)/300 sqft (0.14 liters/ m ).
2
It can be applied using an airless sprayer, brush, or phenolic Mix no more material than can be used within 20 minutes.
®
resin core roller. Themecoat Polyprime 130 is difficult to clean up after it has
cured.
Allow no more material than can be used within 20 minutes.
®
Allow Themecoat Polyprime 130 to become nearly tack Mix no more material than can be used within 20 minutes.
free before applying the coating. Recommended surface
temperature should be greater than 50°F (10°C). If Themecoat WARNING
®
Polyprime 130 is allowed to dry completely, re-prime the This product contains Isocyanate.