Page 13 - tmp

TECHNICAL DATA SHEET
THEMECOAT 759
®
Two Component Modified
Polyurea Protective Coating

PRODUCT DESCRIPTION TECHNICAL DATA (Based on Draw Down Films)
Themecoat 759 is a two component, 1:1, 100% solids,
®
elastomeric, fast set, liquid applied, modified polyurea liner Mix Ratio by Volume 1A : 1B
system for metal, concrete, fiberglass and wood surfaces. It Pot Life 2-5 seconds
is especially designed for high impact at low temperatures
without cracking. Tack Free Time 10-30 seconds
FEATURES Recoat Time 0-12 hours
• Abrasion and Impact Resistant Viscosity at 150-160ºF (66.5-71ºC) , Brookfield:
Side-A
• Chemical Resistant Side-B 120 ± 20 cps
60 ± 20 cps
• High Build Density (Side A & Side B Combined) 9.1 lbs/gal
• Low Temperature Flexibility (1090 kg/m³)
• Quick Drying Flash Point > 200°F (>93.3°C)
• Seamless
• Tough and Elastomeric Hardness, ASTM D-2240 50 ± 5 Shore D
2400 ± 300 psi
TYPICAL USES Tensile Strength, ASTM D-412* (16.5 ± 2.07 MPa)
• Boat Linings Elongation, ASTM D-412* 250 ± 20%
• Cargo Holds
400 ± 40 pli
• Containment Areas Tear, ASTM D-412* (70.1 ± 7.1 kN/m)
• Encapsulation of Fiberglass Bodies and Polystyrene Service Temperature -20ºF - 250ºF
Foams (-29ºC to 121ºC)
• Horse Trailers Water Vapor Permeabilit, ASTM E-96 0.2338 perm-inch
• Industrial Flooring
• Utility Vehicles VOC Content 0 gm/l
• Walkways Recommended Applied Thickness > 2mm (0.2 cm)
• Waterproof Decking Return to Service:
Foot Traffic 1-4 hours
PACKAGING Full Service > 24 hours
10-gallon kit: 5 gallon (47 lbs or 21 kgs net) pail of Side-A, 5 Taber Abrasion Resistance, ASTM D44060
gallon pail (43 lbs or 19.5 kgs net) of Side-B (CS17 wheel, 1000 cycles, 1kg load)(maximum) 2.8 mg loss
100-gallon kit: One 50 gallon (477 lbs or 216 kgs net) drum of Water Asorption, ASTM D471
Side-A, one 50 gallon drum (420 lbs or 191 kgs new) of Side-B (Maximum 74ºF [23ºC], 24 hours) < 0.5%
COLORS Crack Bridging, ASTM C836
Gray and Tan (-13ºF [-25ºC], 1.6 mm crack 25 Cycles) Pass
Impact Resistance @ 74ºF (23ºC) ASTM G14 > 200 lbs
Due to its aromatic composition, Themecoat 759 will tend to
®
yellow or darken in color and will become flat after expo- sure Pull off Strength (Minimum) ASTM D4541
to UV light. Themecoat 759 may be topcoated within twelve Inter-Coat Adhesion (Within recoat time) Excellent
®
hours of application with an aliphatic polyurethane/ polyurea Concrete (Shot-blasted profile) Substrate Failure >500 psi (3.5 MPa)
Concrete (Primed) Substrate Failure at
coating for a colorfast finish. Steel (um blast profile) >500 psi (3.5 MPa)
>900 psi (>6.2 MPa)
COVERAGE Lineal Shrinkage 1-2%
®
Themecoat 759 may be applied at any rate to achieve desired
thickness. Theoretical coverage for 1 mil thickness is one Flexibility (3 mm Mendrel Bend Test) ASTM PASS
D1737
gallon per 1600 sqft (3.78 liters per 149 sqm).
Resistance to Weathering, ASTM G-23 No cracking or
SURFACE PREPARATION Type QUV Weatherometer-2000 hrs exposure blistering
In general, coating performance and adhesion are directly Gloss reduction &
proportional to surface preparation. Most failures in the Minor chalking are
performance of surface coatings can be attributed to poor noted
surface preparation. Polyurea coatings rely on the structural For project-specific questions, contact Polycoat.
strength of the substrate to which they are applied. All surfaces
must be free of dust, dirt, oil, grease, rust, corrosion and NEW AND OLD CONCRETE
other contaminants. When coating substrates previously Refer to SS PC-SP13/NACE 6, or ICRI 03732: CSP 3-5. New
used, it is important to consider the possibility of substrate concrete must be cured for 28 days prior to product application.
absorption, which may affect the adhesion of the coating Surface must be clean, dry, sound and offer sufficient profile
system, regardless of the surface preparation. Polycoat for product adhesion. Remove all dust, dirt, oil, form release
recognizes the potential for unique substrates from one project agents, curing compounds, salts, efflorescence, laitance and
to another. The following information is for general reference. other foreign matter by shotblasting and/or suitable chemical

POLYCOAT PRODUCTS TEL 562.802.8834 | FAX 562.921.7363