Page 9 - Polycoat 10.2 Technical Data Sheet Polycaulk 82

TECHNICAL DATA SHEET
®
POLYEURO LP-11
Two Component Modified Polyurea Protective Coating

Product Description
Polyeuro LP-11 is a two component, 1:1, 100% solids, fast Technical Data (Based on Draw Down Film)
®
set, liquid applied, modified polyurea liner system for metal, Mix Ratio by Volume 1A : 1B
concrete, fiberglass and wood surfaces. Pot Life @ 80ºF (26ºC) 12-16-Seconds
Features Tack Free Time (150 mils thickness) 40-60 Seconds
Recoat Time 6 - 12 hours
• Abrasion and Impact Resistant
• Chemical Resistance Viscosity at 80°F (26°C), Brookfield 400-500 cps
Side-A
• High Build Side-B 700-900 cps
• Low Pressure Application Density (Side-A & Side-B Combined) 9.22 lbs/gal
• Low Temperature Flexibility
• Quick Drying Flash Point > 200°F (93.3°C)
• Seamless Hardness, ASTM D2240 91-93 Shore A
• Tough and Elastomeric Tensile Strength, ASTM D412* 2000 ± 300 psi
13.78 ± 2.07 MPa
Typical Uses Elongation, ASTM D412* 250% ± 50%
• Boat Linings Tear Resistance, ASTM D412* 175 ± 25 pli
• Cargo Holds 30.6 ± 4.37 kNm
• Cargo Liners Service Temperature Dry -20ºF to 200ºF
• Encapsulation of Fiberglass Bodies -30ºC - 93ºC
• Horse Trailers NOTE: Above physicals are from lab drawn films. Actual spray physicals may vary.
• Mold Castings
• Truck-Bed Surfaces strength of the substrate to which they are applied. All sur-
• Utility Vehicles faces must be free of dust, dirt, oil, grease, rust, corrosion
• Walkways and other contaminants. When coating substrates previously
• Waterproof Decking used, it is important to consider the possibility of substrate
absorption, which may affect the adhesion of the coating
Packaging system, regardless of the surface preparation. Polycoat
recognizes the potential for unique substrates from one project
10-gallon kit 5 gallons (18.9 liters) Side-A and 5 to another. The following information is for general reference,
gallons (18.9 liters) Side-B and for project-specific questions, contact Polycoat.
NEW AND OLD CONCRETE
100-gallon kit 50 gallons (189 liters) Side-A and 50 Refer to SSPC-SP13/NACE 6, or ICRI 03732: CSP 3-5. New
gallons (189 liters) Side-B concrete must be cured for 28 days prior to product applica-
tion. Surface must be clean, dry, sound and offer sufficient
profile for product adhesion. Remove all dust, dirt, oil, form
Colors release agents, curing compounds, salts, efflorescence,
Clear/Neutral or Black. Custom colors are available upon laitance and other foreign matter by shotblasting and/or
request. Color packs, when used, must be added to Side-B. suitable chemical means, in accordance with local chemical
Due to its aromatic composition, Polyeuro LP-11 will tend to regulations. Rinse thoroughly, to achieve a pH between 8.0
®
yellow or darken in color after exposure to UV light. Polyeuro and 11.0. Allow to dry completely. If old concrete has a surface
®
LP-11 may be topcoated within twelve hours of application that has deteriorated to an unacceptably rough surface,
with an aliphatic polyurethane/polyurea coating for a colorfast Polycoat Products PC-260 or a mixture of Polyprime 21 and
finish. sand should be used as a repair agent for cracks, spalls, bug
holes and voids. Upon full cure of the repair agent, prime
Coverage the entire surface intended for coating.
Polyeuro LP-11 may be applied at any rate to achieve desired CONCRETE SURFACE PREPARATION REFERENCE
®
thickness. Theoretical coverage for 1 mil (0.254 microns) ASTM D4258 - Standard practice for cleaning concrete
thickness is one gallon per 1600 sqft (3.78 liters per 149 sqm). ASTM D4259 - Standard practice for abrading concrete
Estimating Formula: (1600 sqft per gal /Dry Mil Thickness) x ASTM D4260 - Standard practice for etching concrete
Solids Content = Application Rate per gallon. ASTM F1869 - Standard test method for measuring moisture
vapor emission rate of concrete
Surface Preparation ICRI 03732 - Concrete surface preparation
In general, coating performance and adhesion are directly
proportional to surface preparation. Most failures in the WOOD
performance of surface coatings can be attributed to poor All wood should be clean, dry and free of any knots, splinters,