TECHNICAL DATA SHEET
®
THEMECOAT 756
Two Component Modified
Polyurea Protective Coating

PRODUCT DESCRIPTION
Themecoat 756 is a two component, 1:1 mix, 100% solids, TECHNICAL DATA (Based on Draw Down Films)
®
fast set, liquid applied, modified polyurea liner system for Mix Ratio 1A : 1B
metal, concrete, fiberglass and wood surfaces.
Pot Life 3-5 seconds
Tack Free Time 20-40 seconds
FEATURES
• Abrasion and Impact Resistant Recoat Time 0-12 hours
• Chemical Resistant Viscosity at 150-160ºF
• High Build (66.6-71ºC), Brookfield: 120 ± 20 cps
Side-A
• Low Temperature Flexibility Side-B 200 ± 20 cps
• Quick Drying Density (Side A & B 9.0 lbs/gal
• Seamless Combined) (1180 kgs/m )
3
• Tough and Elastomeric
Flash Point >200ºF
(>93.3ºC)
TYPICAL USES Hardness, ASTM D-2240* 85 ± 5 Shore A
• Architectural Shapes Tensile, ASTM 412-C* 1500 ± 300 psi
• Decorations (10 ± 2.1 MPa)
• Encapsulation of Fiberglass Bodies and Polystyrene Elongation, ASTM 412-C* 200% ± 20%
Foams
• Tree Bark Tear, ASTM 624-C* 200 ± 20 pli
(35 ± 3.5 kN/m)
PACKAGING Service Temperature - Dry -20ºF to 250ºF
10-gallon kit: 5 gallon (18.9 liters) pail of Side-A and 5-gallon (-29 to121ºC)
(18.9 liters) pail of Side-B. (*These physical properties from sample sprayed with Graco Foam Cat
106-gallon kit: 53 gallon (200 liters) drum of Side-A and 200 @ 2000 psi (32 MPa) minimum, with Gusmer GX7-400 mechanical
purge gun @ 150-160°F (66-72ºC). Different machine and parameter will
53-gallon (200 liters) drum of Side-B. change these properties. User should perform their own independent
testing as properties are approximate).
COLORS
Neutral or Black. Custom colors are available upon request.
Additional charges may apply.

MIXING to ensure proper adhesion and good surface appearance.
Themecoat 756 may not be diluted under any circumstances. Abrasive blast using brush blast technique or better to achieve
®
Thoroughly mix Themecoat 756 Side-B Base material with 1.5-3 mil (37-75 microns) anchor profile.
®
air driven power equipment until a homogeneous mixture
and color is obtained. Vacuum to remove dust, etc., prior to application of primer.
Use fiberglass (C-Veil Glass) or a geotextile cloth to bridge
cracks over the primed surface.
COVERAGE Primer is always recommended to take care of voids, pot
Themecoat 756 may be applied at any rate to achieve desired holes or bug holes etc.
®
thickness. Theoretical coverage per gallon is 1600 sqft at 1 mil.
APPLICATION
SURFACE PREPARATION Themecoat 756 Side-A and Side-B materials should be
®
In general, coating performance and adhesion are directly preconditioned at 75-80°F (24-27°C) before application.
proportional to surface preparation. All surfaces must be free Themecoat 756 should be applied using a plural component,
®
of oil, grease, dirt and other contaminants.
heated, high pressure 1:1 spray mixing equipment like Graco’s
CONCRETE Hydra Cat, Gusmer or other equivalent ma- chine may be used.
Remove all contaminants such as oil, grease, dirt, form oil Both Side-A and Side-B materials should be sprayed at
residue, wax or any other chemical product prior to proceeding temperatures above 150°F (66°C). Adequate pressure and
with surface preparation. The surface should be free of voids, temperature should be maintained at all times.
pot holes or bug holes, loose or weak concrete and the
necessary surface profile must be achieved as listed below