TECHNICAL DATA SHEET | Section 9.2
®
POLYEURO 5801-FR
Two Component, Aromatic, Polyurea Protective Coating

Product Description
Polyeuro 5801-FR is a fast setting, rapid curing, 100% solids, Technical Data (Based on Draw Down Film)
®
flexible, aromatic, two component spray polyurea that can Mix Ratio by Volume 1A : 1B
be applied to suitably prepared concrete and metal surfaces. Pot Life @150-160ºF (65.5-71ºC), 50% R.H. 4 - 8 seconds
It may be applied in single or multiple applications without
appreciable sagging and is relatively insensitive to moisture Tack Free Time (thickness & substrate 45-60 seconds
and temperature allowing application in most temperatures. temperature dependent)
Polyeuro 5801-FR offers a tack free time of less than 10 Recoat Time 0 - 6 hours
®
minutes and exhibits 350% ± 50% elongation upon curing Viscosity at 150-160°F (66.5-71°C)
with 80 Shore A hardness. Side-A 100 ± 20 cps
Side-B 50 ± 20 cps
Features
Density (Side A & B Combined) 8.81 lbs/gal
• Coats Carbon or Mild Steel Metals Without Primer
Flash Point > 200°F (93.3°C)
• Elastomeric
Hardness, ASTM D2240 80 ± 5 Shore A
• Excellent Thermal Stability
Tensile Strength, ASTM D412* 1500 ± 200 psi
• Good Chemical Resistance 10.34 ± 1.37 MPa
• Installed With or Without Reinforcement in Elongation, ASTM D412* 350 ± 50%
Transitional Areas Tear Resistance, ASTM D412* 250 ± 30 pli
• Low Temperature Flexibility 43.8 ± 5.3 kNm
• Meets ASTM E84 Class 1 Fire Test Criteria* Service Temperature - Dry -40°F to 250°F
-40°C to 121°C
• Meets USDA Criteria
Service Temperature - Wet 40°F to 120°F
• Odorless 4.44°C to 48.89°C
• Seamless Burn Testing Class 1 ASTM E84 Passed
(@20 mil or less)
• Zero VOC (100% Solids)
(*These physical properties from sample sprayed with Graco EXP2 @ 2000 psi minimum, with
Fusion Gun AR4242 @ 150-160°F (65°C to 71°C). Different machine and parameter will change
these properties. User should perform their own independent testing as properties are approximate).
Typical Uses
• Airports • Power Plants
• Cold Storage Facilities • Refineries Colors
• Secondary Containment Clear/Neutral. Custom colors are available upon request.
• Fertilizer Plants
• Walkways and Balconies Color Packs, when used, must be added to Side-B.
• Food Processing Plants • Warehouse Floors Due to its aromatic composition, Polyeuro 5801-FR will tend to
®
• Industrial and • Water and Wastewater yellow or darken in color and will become flat after exposure
®
Manufacturing Treatment Plants to UV light. A topcoat can be applied to Polyeuro 5801-FR
Facilities within six hours of application with an aliphatic polyurethane/
polyurea coating for a colorfast finish.
• Landfill Containment
Coverage
• Marine Environments Polyeuro 5801-FR may be applied at any rate to achieve
®
• Mining Operations desired thickness. Theoretical coverage for 1 mil (0.254
microns) thickness is one gallon per 1600 sqft (3.78 liters per
• Paper and Pulp Mills 149 sqm).
Estimating Formula: (1600 sqft per gal /Dry Mil Thickness) x
Solids Content = Application Rate per gallon.
Packaging Surface Preparation
In general, coating performance and adhesion are directly
10-gallon kit 5 gallons (18.9 liters) Side-A proportional to surface preparation. Most failures in the
(Isocyanate side) and 5 gallons (18.9 performance of surface coatings can be attributed to poor
liters) Side-B (Resin side) surface preparation. Polyurea coatings rely on the structural
strength of the substrate to which they are applied. All surfaces
must be free of dust, dirt, oil, grease, rust, corrosion and other
100-gallon kit 50 gallons (189 liters) Side-A contaminants. When coating previously used substrates, it is
(Isocyanate side) and 50 gallons (189 important to consider the possibility of substrate absorption,
liters) Side-B (Resin side)

POLYCOAT PRODUCTS TEL 562.802.8834 | FAX 562.921.7363 Section 9.2
wpsales@polycoatusa.com | www.polycoatusa.com